List of Plastic Materials Tests
02-04-2018
Pipe tests
CEISLAB carries out the following analysis and characterization tests. All accredited by ENAC in accordance with the standard ISO 17025.
| PRODUCTS/MATERIALS TESTED | TYPE OF TEST | STANDARD SPECIFICATIONS/ TEST PROCEDURE | |
|---|---|---|---|
| Polyethylene (PE) pipes and fittings | Determination of the tensile strength and failure mode of test pieces from a butt-fused joint | UNE-ISO 13953:2011 | |
| Crushing decohesion test | ISO 13955:1997 | ||
| Peel decohesion test electrofusion assemblies of nominal outside diameter greater than or equal to 90 mm | ISO 13954:1997 | ||
| Copolymer pipes of polipropylene | Resistance to impact strength by the Charpy method (Energy 15J) | ISO 9854-1:1994ISO 9854-2:1994 | |
| Thermoplastics pipes and fittings (completed mouthpieces are included) | Determination of the resistance to internal pressure at a constant temperature(Maximum pressure: 100 bar)
(Maximum temperature: 110°C) |
UNE-EN ISO 1167-1:2006 UNE-EN ISO 1167-2:2006 UNE-EN ISO 1167-3:2008 UNE-EN ISO 1167-4:2008 |
|
| Injection-moulded thermoplastics fittings | Visually assessing the effects of heating (heat behaviour) | UNE-EN ISO 580:2005 Method A. Section. A |
|
| Structured-wall thermoplastics pipes | Heater test for structured wall pipes | ISO 12091:1995 | |
| Thermoplastic pipes of circular transversal section | Test method for resistance to external blows by the round-the-clock method (0°C) | UNE-EN 744:1996 UNE-EN 744:1996 ERRATUM UNE-EN 744:1997 ERRATUM EN 744:1995 |
|
| Thermoplastics pipes | Longitudinal reversion (Air oven method) |
|
|
| Polyethylene pipes for water supply for irrigation | Cracking by tension in active environment | UNE 53367-1:2014 Section.5.4.2 | |
| Thermoplastics pipes | Determination of tensile properties(Maximum force: 10 kN) | UNE-EN ISO 6259-1:2002 UNE-EN ISO 6259-1:2015 UNE-EN ISO 6259-3:2015 ISO 6259-1:1997 ISO 6259-1:2015 ISO 6259-2:1997 ISO 6259-3:1997 ISO 6259-3:2015 |
|
| Determination of resistance to external blows. Round-the-clock method | ISO 3127:1994 | ||
| Polyolefin pipes | Determination of resistance to crack propagation | UNE-EN ISO 13479:2010 | |
| Plastics piping systems elastomericsealing-ring-type socket joints of unplasticized poly (vinil chloride)(PVC-U) for use with pvc-u pipes. | Test method for leaktightness under negative pressure(dn ≤ 315) | UNE-EN ISO 13844:2001 UNE-EN ISO 13844:2015 |
|
| Test method for leaktightness under internal pressure and with angular deflection(dn ≤ 315) |
|
||
| Plastics piping systems – End-loadbearing and non-end-load-bearing assemblies and joints for thermoplastics pressure piping | Test method for long-term leaktightness under internal water pressure.(dn ≤ 315) | UNE-EN ISO 13846:2001 | |
| Plastic pipes systems | Test method for leaktightness under vacuum | ISO 13056:2011 | |
| Plastics piping and ducting systems | Determination of the long-term hydrostatic strength of thermoplastics materials in pipe form by extrapolation | UNE-EN ISO 9080:2013 | |
| Plastic Pipes Systems | Tensile strength of the joints | UNE 53008-1:2014 Annexs B, D, E, F, G, H, I |
|
| Crush test | |||
| Impact resistance test on joints | |||
| Thermal cycling resistance | |||
| Repeated bending test | |||
| Adhesion and cracking for expansion test | |||
| Thermal durability of the outer layer of M-pipes | |||
| Thermoplastics piping systems for non-pressure applications | Test method for watertightness.(dn ≤ 315) | UNE-EN 1053:1996 ISO 13254:2010 |
|
| Test method for airtightness of joints.(dn ≤ 315) | UNE-EN 1054:1996 ISO 13255:2010 |
||
| Test methods for leaktightness of elastomeric sealing ring type joints(dn ≤ 315) | UNE-EN 1277:2004 UNE-EN 1277:2004 ERRATUM:2006 ISO 13259:2010 |
||
| Thermoplastics pipes for the conveyance of fluids | Determination of resistance to rapid crackpropagation (RCP) – Small-scale (For dn 110 SDR 11 and dn250 SDR 11) | UNE-EN ISO 13477:2008 | |
| Thermoplastic pipes | Determination of ring flexibility(dn ≤ 630) | UNE-EN ISO 13968:2009 | |
| Determination of the ring stiffness(dn ≤ 630) | UNE-EN ISO 9969:2016 | ||
| Determination of creep ratio(dn ≤ 630) | UNE-EN ISO 9967:2016 | ||
| Plastics piping systems and plasticscomponents | Dimensional control (Thickness and external diameter) | UNE-EN ISO 3126:2005 Section.5.2 y 5.3 UNE-EN ISO 3126:2005 ERRATUM 2007 |
|
| Plastics piping systems | Test method for the adhesion of the different layers using a pulling rig | UNE-EN ISO 17454:2007 UNE 53008-1:2014 Annex C RP01.71 REV 03 Annex F |
|
| Test method for the resistance of mounted assemblies to temperature cycling<63 cm | UNE-EN 12293:2000 ISO 19893:2011 |
||
| Test method for resistance of joints to pressure cycling(23 ± 5°C) | UNE-EN 12295:2000 ISO 19892:2011 |
||
| Test method for leaktightness under vacuum | UNE-EN 12294:2000 | ||
| Test method for resistance to pull-out under constant longitudinal force | UNE-EN ISO 3501:2015 | ||
| Test method for leaktightness under internal pressure of assemblies subjected to bending | UNE-EN ISO 3503:2015 | ||
| Plastics | Determination of ash | UNE-EN ISO 3451-1:2008 Method A EN ISO 3451-1:2008 Method A |
|
| Polyethilen pipes | Cone test method | ISO 13480:1997 | |
| Plastics piping and ducting systems.Thermoplastics pipes. | Determination of resistance to external blows by the staircase method | UNE-EN 1411:1996 | |
| Plastics | Determination of water content | UNE-EN-ISO 15512:2010 UNE-EN ISO 15512:2015 UNE-EN ISO 15512:2017 Method B |
|
| Flexible hose assemblies in drinking wáter installations | Ammonia test for stress corrosion resistance | ISO 6957:1988 UNE-EN 13618:2017 Annex A.2 |
|
| Plastics pipes and fittings | Determination of opacity | UNE-EN ISO 7686:2006 EN ISO 7686:2005 |
|
| Plastics piping and ducting systems.Polyolefin pipes and fittings. | Determination of oxidation induction time | UNE-EN 728:1997 ISO 11357-6:2008. Except sections . 4.3, 8.2 y 9.6.2 |
|
| Polyolefines with carbon black content up to 3% | Carbon black dispersion. Compression method | ISO 18553:2002 ISO 18553:2002/Addendum:2007 |
|
| Thermoplastic materials | Determination of the melt mass-flow rate (MFR)(Temperatura: 190°C y 230°C) | UNE-EN ISO 1133-1:2012 | |
| Polyethylene piping materials and components | Determination of volatile content. | UNE-EN 12099:1997 | |
| Pipes made of crosslinked polyethylene (PE-X) | Estimation of the degree of crosslinking by extraction with dissolvents | UNE-EN ISO 10147:2014 | |
| Unplasticized poly(vinyl chloride)(PVC-U) pipes | Test method for the resistance to dichloromethane at a specified temperature (DCMT) (15°C) | UNE-EN 580:2003 ISO 9852:2007 |
|
| Polyolefins and its products | Carbon black content | ISO 6964:1986 UNE 53375-1:2007 |
|
| Cylindric thermoplastic pipes with flat surfaces | Determination of residual vinyl chloride monomer in PVC resins(0,5 mg/kg – 2 mg/kg) | UNE-EN ISO 6401:2009 | |
| Thermoplastics pipes and fittings | Determination of Vicat softening temperature (VST). (Maximum temperature: 120°C) | UNE-EN 727:1995 ISO 2507-1:1995 |
|
| Non-cellular plastic materials | Determination of density by immersion method | UNE-EN ISO 1183-1:2013 Method A Section 5.1 |
|
| Determining the density and the relative density by picnometer method |
|
||
| Elastomeres | Salt spray tests | UNE-EN ISO 9227:2012 | |
| Flexible insulating sleeving | Determination of low levels of fluorine(0,02-0,35)% | EN 60684-2:2011 IEC 60684-2-Ed.3 2011-08 Method B Section 45.2 |